KmTBCr26 anti-wear white cast iron

KmTBCr26 high chromium cast iron can be used in different occasions and is especially suitable for wear-resistant environments, such as power plants, ore processing plants and steel mills, etc. Its excellent wear resistance is due to the high volume fraction of high hardness carbides. It is generally believed that the original coarse carbides can sharply reduce the toughness of the material, so the application of hypereutectic alloys is limited. However, recent studies have shown that the fracture toughness of hypereutectic high chromium cast iron with a small amount of primary M 7C3 carbides is higher than that of hypoeutectic alloys [1]. Mechanical properties of cast iron [2-4]. The research in this paper involves the development of excellent wear-resistant materials, so we have carried out a series of basic theoretical studies on the phase diagram, solidification process, hardenability and mechanical properties of high-chromium cast iron.

  • kmtbcr26 anti wear white cast iron 05
  • kmtbcr26 anti wear white cast iron 04
  • kmtbcr26 anti wear white cast iron 03
  • kmtbcr26 anti wear white cast iron 02
  • kmtbcr26 anti wear white cast iron 01

An additional oxidation test was carried out on the two alloys at 923K (650~C), and the oxidation weight is negligible relative to the wear weight loss, so the oxidation effect is negligible in the calculation of the wear test research in this paper. The wear rates of the two alloys begin as an unstable cycle, and then a stable cycle, as shown in Figure 5. The average wear rate of the test alloy is 36% of the standard 25Cr cast iron, which shows that the test alloy has excellent wear resistance at high temperature. Observation of the wear surface of 25C r cast iron by scanning electron microscope shows that the wear of the alloy is related to its metallographic structure. When the wear test is carried out at the test temperature, the soft primary r phase is quickly worn away, and the remaining hard eutectic carbide phase forms a hilly wear surface due to its high wear resistance. Observation with a scanning electron microscope at a large magnification shows that the wear mechanism of the primary r phase is the generation of micro grooves and deformation, while the wear mechanism of the eutectic carbide is a brittle fracture process. Oxidation does not significantly affect the wear of these alloys. Compared with the 25Cr cast iron standard alloy sample, the wear pattern of the test alloy sample is quite smooth, indicating that the primary phase and eutectic carbide prevent the wear of the quartz sand at the test temperature, and it can be inferred that the brittle fracture process controls the wear of the sample. It was also observed that oxidation on the worn surface of the samples resulted in the expansion of carbonaceous carbides, thus indicating that the oxidation process aggravates the wear of these alloys.

Chemical composition of GB-KmTBCr26

C(%) Si(%) Mn(%) P(%) S(%) Cr(%) Mo(%) Ni(%) Cu(%)
2.3-3.0 ≦1.0 0.5-1.0 ≦0.1 ≦0.06 23.0-28.0 0.0-1.0 0.0-1.5 0.0-2.0

Applications

  • Abrsion Resisting Cast lron Low Alloy and High Alloy Grade

Country Code

  • GB

Standard

  • 8263

Steel Type

  • KmTBCr26

Abrasion Resisting Cast Iron Low Alloy and High Alloy Grade

Chemical compsition

Standard Item Grade Chemical composition (%)
C Si Mn P S Ni Cr Mo Cu
GB 8263 KmTBNi4-Cr2-DT 2.7-3.2 0.3-0.8 0.3-0.8 ≦0.15 ≦0.1 3.0-5.0 2.0-3.0 0.0-1.0
ASTM A532 I BNiCr-LC 2.4-3.0 ≦0.8 ≦2.0 ≦0.3 ≦0.15 3.3-5.0 1.4-4.0 ≦1.0
DIN 1695 G-X260-NiCr42 2.6-2.9 0.2-0.8 0.3-0.7 3.5-5.0 1.4-2.4 ≦0.5
GB 8263 KmTBNi4-Cr2-GT 3.2-3.6 0.3-0.8 0.3-0.8 ≦0.15 ≦0.1 3.0-5.0 2.0-3.0 0.0-1.0
ASTM A532 I ANCr-HC 2.8-3.6 ≦0.8 ≦1.3 ≦0.3 ≦0.15 3.3-5.0 1.4-4.0 ≦1.0
DIN 1695 G-X330-NiCr42 3.0-3.6 0.2-0.8 0.3-0.7 3.3-5.0 1.4-2.4 ≦0.5
GB 8263 KmTBCr9-Ni5Si2 2.5-3.6 1.5-2.2 0.3-0.8 ≦0.15 ≦0.1 4.5-6.5 8.0-10.0 0.0-1.0
ASTM A532 I DNiHCr 2.5-3.6 ≦2.0 ≦2.0 ≦0.1 ≦0.15 4.5-7.0 7.0-11.0 ≦1.5
DIN 1695 G-X300Cr-NSi952 2.5-3.5 1.5-2.2 0.3-0.7 4.5-6.5 8.0-10.0 ≦0.5
GB 8263 KmTBCr15-Mo2-GT 2.8-3.5 ≦1.0 0.5-1.0 ≦0.1 ≦0.06 0.0-1.0 13.0-18.0 0.5-3.0 0.0-1.2
ASTM A532 ⅡB15%Cr-Mo-HC 2.0-3.0 ≦1.5 ≦2.0 ≦0.1 ≦0.06 ≦2.5 14.0-18.0 1.0-3.0 ≦1.2
DIN 1695 G-X300-CrMo153 2.3-3.6 0.2-0.8 0.5-1.0 ≦0.7 14.0-17.0 1.0-3.0 ≦1.2
ASTM A532 Ⅱ020%-CrMo-LC 2.0-3.3 1.0-2.2 ≦2.0 ≦0.1 ≦0.06 ≦1.5 18.0-23.0 ≦2.0 ≦1.2
DIN 1695 G-X260Cr-MoNi2021 2.3-2.9 0.2-0.3 0.5-1.0 0.8-1.2 18.0-22.0 1.4-2.0
GB 8263 KmTBCr20-Mo2Cu1 2.0-3.0 ≦1.0 0.5-1.0 ≦0.1 ≦0.06 0.0-1.5 18.0-22.0 1.5-2.5 0.8-1.2
ASTM A532 ⅡA-25%Cr 2.0-3.0 ≦1.5 ≦2.0 ≦0.1 ≦0.06 ≦2.5 23.0-30.0 ≦3.0 ≦1.2
DIN 1695 G-X260-Cr27 2.3-2.9 0.5-1.5 0.5-1.5 ≦1.2 24.0-28.0 ≦1.0
GB 8263 KmTBCr26 2.3-3.0 ≦1.0 0.5-1.0 ≦0.1 ≦0.06 0.0-1.5 23.0-28.0 0.0-1.0 0.0-2.0
ASTM A532 Ⅲ A-25%Cr 2.0-3.3 ≦1.0 ≦2.0 ≦0.1 ≦0.06 ≦2.5 23.0-30.0 ≦1.5 ≦1.2
DIN 1695 G-X300Cr-Mo271 3.0-3.5 0.2-1.0 0.5-1.0 23.0-28.0 1.0-2.0 ≦1.2

Physical properties & Hardness

Standard Item Grade Tensile requirements Hardness(HB)
Thickness(mm) Tensile strength(Mpa) Elongation(%) Heat treatment
GB 8263 KmTBNi4-Cr2-DT
ASTM A532 I BNiCr-LC ≧200 ≦550
DIN 1695 G-X260-NiCr42 ≧320 ≦500
GB 8263 KmTBNi4-Cr2-GT
ASTM A532 I ANCr-HC ≧200 ≦550
DIN 1695 G-X330-NiCr42 ≧280 ≦690
GB 8263 KmTBCr9-Ni5Si2
ASTM A532 I DNiHCr ≧300 ≦500
DIN 1695 G-X300Cr-NSi952 500-600 ≦690
GB 8263 KmTBCr15-Mo2-GT
ASTM A532 ⅡB15%Cr-Mo-HC ≧75 H ≦600
DIN 1695 G-X300-CrMo153 ≧450 ≦690 H
ASTM A532 Ⅱ020%-CrMo-LC ≧200 H ≦600
DIN 1695 G-X260Cr-MoNi2021 ≧450 H ≦690
GB 8263 KmTBCr20-Mo2Cu1
ASTM A532 ⅡA-25%Cr ≧200 ≦600
DIN 1695 G-X260-Cr27 ≧560 ≦690
GB 8263 KmTBCr26
ASTM A532 Ⅲ A-25%Cr ≧200 H ≦600
DIN 1695 G-X300Cr-Mo271 ≧450 H ≦690