Alloy 410 (UNS S41000) is a 12% chromium martensitic stainless steel plate that can be heat treated to obtain a wide range of mechanical properties. The alloy has good corrosion resistance along with high strength and hardness. In the annealed condition, 410 stainless steel plate is ductile and may be formed.

410 stainless steel is a hardenable martensitic stainless steel alloy. Unlike austenitic grades it can be heat treated (“quench and temper”) to generate high strength with good ductility. 410 alloy is required when strength, hardness and wear resistance is required with some corrosion resistance.

Due to the hardening capabilities of this steel, other properties and the resulting performance of this material are somewhat compromised. The alloy can only effectively be used in mildly corrosive environments. The operating temperature range is limited a) a loss of strength by over tempering at elevated temperatures and b) a loss of ductility at sub-zero temperatures.

Type 410 is officially a stainless steel but characteristically the material is actually a compromise of high carbon steel alloy (which promotes wear resistance) with chromium stainless steel (which promotes corrosion resistance).

This steel is ideal for use in the manufacture of highly stressed parts found in a variety of industries including petrochemical, automotive and power generation.

Chemical composition of 410 stainless steel

UNS No	S41000
EN	1.4006
AISI	410
Carbon (C)	0.08/0.15
Silicon (Si)	1
Manganese (Mn)	1.5
Phosphorus (P)	0.04
Sulphur (S)	0.03
Chromium (Cr)	11.5/13.5
Molybdenum (Mo)
Nickel (Ni)	0.75
Nitrogen (N)

410 stainless steel provides good corrosion resistance as well as high strength and hardness. It is magnetic in both the annealed and hardened conditions. Grade 410 stainless steel is a hardenable, martensitic stainless steel that features a minimum addition of 11.5% chromium.

Mechanical properties of 410 stainless steel

DESCRIPTION	TYPE 410
Proof Stress 0.2% (MPa)	205
Tensile strength (MPa)	450
Elongation A5 (%)	20
Hardness	HB: 217 HRB: 96

Alloy 410 (AMS 5504) is magnetic in both the annealed and hardened conditions.

410/HT Stainless Steel

Alloy 410HT is the basic, general purpose, heat treated version of Type 410. It is a martensitic type, used for general purpose, where corrosion is not severe. Alloy 410 contains a minimum of 11.5% chromium which is just sufficient enough to demonstrate corrosion resistance properties in mild atmospheres, steam, and many mild chemical environments.

Chemical composition of 410 HT stainless steel

UNS No	S41000
EN	1.4006
AISI	410
Carbon (C)	0.15
Silicon (Si)	1.0
Manganese (Mn)	1.0
Phosphorus (P)	0.04
Sulphur (S)	0.03
Chromium (Cr)	11.5/13.5
Molybdenum (Mo)
Nickel (Ni)	0.5
Nitrogen (N)

Mechanical properties of 410/HT stainless steel

DESCRIPTION	TYPE 410
Proof Stress 0.2% (MPa)	205
Tensile strength (MPa)	450
Elongation A5 (%)	20
Hardness	HB: 217 HRB: 96

Alloy 410 (AMS 5504) is magnetic in both the annealed and hardened conditions.

Applications requiring moderate corrosion resistance and high mechanical properties are ideal for Alloy 410HT. Examples of applications that frequently used Alloy 410HT include: