GB/T 3077 12Cr1MoV steel has a high thermal strength and anti-oxidant properties, have higher durable plastic. The production process is relatively simple, and good weldability, but normalizing cooling rate sensitive.
The Element Max (%) | Data |
---|---|
C | 0.08~0.15 |
Si | 0.17~0.37 |
Mn | 0.40~0.70 |
P | 0.035 |
S | 0.035 |
Grade | Property | |||
---|---|---|---|---|
Thickness | Yield | Tensile | HB | |
12Cr1MoV | mm | Min Mpa | Mpa | HB |
6-50 | 245 | 490 | ||
50-200 | 245 | 490 |
Compared with 12CrMoV steel, this steel has higher oxidation resistance and thermal strength. The creep limit of the steel is very close to the value of the endurance strength, and it has high plasticity under the condition of the endurance tension. The technology and weldability of the steel are good, but the preheating is required to 300℃ before welding, and the stress is removed after welding.
It is a kind of steel widely used in superheater, header and main steam pipe of high pressure, ultra high pressure, subcritical power station boiler. At 580℃, it still has high thermal strength, oxidation resistance and durable plasticity. The production process is simple and the welding performance is good, but it is sensitive to the normalizing cooling speed. Long-term use at 580℃ will result in the second kind of temper brittleness caused by the segregation of phosphorus and other impurities at grain boundary. Long–term use will also appear pearlite spherification.
All of them are pearlite type heat-resistant steel, which has high tissue stability and thermal strength when used in high temperature for a long time. Compared with 12Cr1MoV steel, Cr content is higher, with higher oxidation resistance and thermal strength. Creep limit is close to the endurance strength value and has higher plasticity under the condition of endurance tension. The technology and weldability of the steel are good, but the preheating is required to 300℃ before welding, and the stress is removed after welding.
12CrMoV and 12Cr1MoV alloy steel, API 5L X52 steel with the thickness range is 1.2-40mm, the width range is 1220-4200mm, and the length range is 5000-18000mm. API 5L X52 steel’s mechanical properties is the yield strength 300MPa, and the tensile strength 460MPa. To be specified in details: Maximum content for C≤0.28%, Mn≤1.4%, P≤0.030%, S is 0.030%, V+Nb+Ti≤0.15%, Copper maximum is 0.50%, nickel maximum 0.50%, chromium 0.50%, Molybdenum 0.15%.
It is very important for a company to have a sound after-sales service system, which better guarantees the interests of customers and increases the reliability of the company’s products in the hearts of customers. Our company has a dedicated after-sales service team and good after-sales service reputation, and has been recognized by customers over the past decades. Whenever there is problem about our 12CrMoV and 12Cr1MoV alloy steel steel materials during application on the user site, our after-sales service persons will assist to find solutions at the first time.